Failure mechanisms of magnesia alumina spinel abradable coatings under thermal cyclic loading

This double-layer system was sprayed onto disc-shaped Inconel 738 superalloy substrates, which were coated with a vacuum plasma sprayed MCrAlY bondcoat. The lifetime of the coating system was assessed via thermal gradient cycling testing with surface temperatures above 1400 °C. During cycling, the samples showed a typical failure mechanism with exfoliation of thin coating lamellae starting from the coating surface. This failure mechanism was not observed in thermal barrier or abradable coatings in the past. The failure mechanism was analysed and mismatch stress calculations were carried out.