Qualitative photoluminescence study of defect activation in telecommunication fibers and Bragg gratings in hydrogen-loaded fibers

Despite the relevance of glass fibers and integrated optical circuits for an increasing number of cutting-edge applications ranging from telecommunication to sensing and quantum photonics, the knowledge about their structural and chemical properties is still in its infancy. Optical spectroscopy techniques are challenged due to the intrinsically low cross-sections for inelastic processes. Our approach is to detect these properties along the core, extending the interaction to the fiber length. We report on in-situ temperature-dependent photoluminescence (PL) measurements in transmission geometry of a) pristine optical glass fibers (standard commercial telecom grade and different types of photosensitive fibers) and b) type I fiber Bragg grating (FBG) in hydrogen-loaded fibers of the same type. A laser with 473 nm wavelength and TEM 00 mode is coupled to an optical spectrometer through different fibers. The fibers are thermally cycled between room temperature and 950° Celsius. As a first observation, we detect a clearly visible red emission from the uncoated fibers at the location of the fiber Bragg grating. Fitting the luminescence spectra with a single Gaussian and monitoring the intensity as a function of temperature reveals an irreversible, thermally activated degradation of the luminescence associated to the fiber Bragg gratings. A closer inspection of pristine glass fibers without FBG revealed a faint, yet thermally stable luminescence with similar spectral characteristics. Analyzing qualitative data for two consecutive heating cycles confirmed two distinct activation energies. This may be due to several reasons such as different defects at the basis of this emission or different structural or chemical environments for the same defect. Further experiment will be carried out in the future to investigate the main reason of two distinct activation energies.