Large Faraday effect of borate glasses with high Tb3+ content prepared by containerless processing

Borate glasses containing a large amount of Tb3+ ions have been prepared by containerless processing. The content of Tb2O3 reached 60 mol%. The glass bearing the highest content of Tb3+ ions showed a large Faraday effect; the Verdet constant was 234 rad/T m. Annealing of the glasses in H2/N2 atmosphere resulted in a low optical absorption coefficient, leading to an extremely large magneto-optical figure of merit that was ∼1.7 times higher than that of Tb3Ga5O12 single crystal.