AC electrical conduction mechanisms and dielectrical studies of DD3 kaolin sintered at high temperature
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
مواد الکترونیکی، نوری و مغناطیسی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: AC electrical conduction mechanisms and dielectrical studies of DD3 kaolin sintered at high temperature AC electrical conduction mechanisms and dielectrical studies of DD3 kaolin sintered at high temperature](/preview/png/7921705.png)
چکیده انگلیسی
In this study, DD3 kaolin, as a raw material, was thermally treated at a temperature ranging from 1000â¯Â°C to 1600â¯Â°C. The X-ray diffraction (XRD) patterns show the appearance of cristobalite and mullite phases at sintered temperature less than 1300â¯Â°C. Moreover, they revealed the formation of mullite at a higher temperature (1600â¯Â°C). The surface of mullite sample (DD3 at 1600â¯Â°C) is showed roughly with prismatic grains having an average size in the range of 32-42â¯nm. The FTIR spectrum is dominated by the stretching Si-O modes and Al-O at the wave number ranging from 443 to 1257â¯cmâ1. The dielectric and electrical properties were investigated in a wide frequency (0.1-10â¯MHz) and at a temperature ranging from 0 to 200â¯Â°C. A strong dispersion of permittivity constants was observed at a low frequency, which can be attributed to interfacial Maxwell-Wagner-Sillar (MWS) relaxation. It is found that the ac conductivity depends on frequency and temperature with the Joncher power law A(T) Ïs. Temperature analysis showed that the electron conductivity is controlled by both the small polaron tunneling (SPT) and the hopping correlated barrier (CBH) models.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Chemistry and Physics - Volume 212, 15 June 2018, Pages 187-195
Journal: Materials Chemistry and Physics - Volume 212, 15 June 2018, Pages 187-195
نویسندگان
Ibrahim Khorchani, Olfa Hafef, Julian J. Reinosa, Adel Matoussi, J.F. Fernandez,