Microstructure and abrasive wear resistance of an alloyed ductile iron subjected to deep cryogenic and austempering treatments

To further improve the mechanical performance of a new alloyed austempered ductile iron (ADI), deep cryogenic treatment (DCT) has been adopted to investigate the effect of DCT time on the microstructure and mechanical behaviors of the alloyed ADI Fe-3.55C-1.97Si-3.79Ni-0.71Cu-0.92Mo-0.64Cr-0.36Mn-0.30 V (in wt.%). With increasing the DCT time, more austenite transformed to martensite and very fine carbides precipitated in martensite in the extended period of DCT. The amount of austenite decreased in alloyed ductile irons, while that of martensite and carbide precipitation increased. The alloyed ADI after DCT for 6 h had the highest hardness and compressive strength, which can be attributed to the formation of more plate-like martensite and the finely precipitated carbides. There was a gradual decrease in hardness and compressive strength with increasing the DCT time to 12 h because of the dissolution of M3C carbide. After tempering, there was a decrease in mechanical properties compared to the direct DCT sample, which was caused by the occurrence of Ostwald ripening of precipitated carbides. The optimum wear resistance was achieved for the alloyed ADI after DCT for 6 h. The wear mechanism of the alloyed ADI in associating with DCT is mainly consisted of micro-cutting wear and some plastic deformation wear.