Fracture mode identification of low alloy steels and cast irons by electron back-scattered diffraction misorientation analysis
ترجمه فارسی عنوان
شناسایی حالت شکستگی از فولادهای آلیاژی کم و آهن ریخته گری با تجزیه و تحلیل ناپیوسته پراکندگی الکترون برگشت پذیر
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
شیمی مواد
چکیده انگلیسی
The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction (EBSD) misorientation analysis in this research. The curves of grain reference orientation deviation (GROD) distribution perpendicular to the fracture surface were obtained by EBSD observation, and the characteristics of each fracture mode were identified. The GROD value of the specimen fractured in tension decreases to a constant related to the elongation of corresponding specimen in the far field (farther than 5Â mm away from the fracture surface). The peak exhibits in GROD curves of two smooth specimens and a notched specimen near the fracture surface (within 5Â mm away from the fracture surface), and the formation mechanisms were discussed in detail based on the influences of specimen geometries (smooth or notched) and material toughness. The GROD value of fatigue fractured specimen is close to that at undeformed condition in the whole field, except the small area near the crack path. The loading conditions (constant stress amplitude loading or constant stress intensity factor range â³K loading) and the EBSD striation formation during fatigue crack propagation were also studied by EBSD observation parallel to the crack path.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Materials Science & Technology - Volume 33, Issue 12, December 2017, Pages 1582-1595
Journal: Journal of Materials Science & Technology - Volume 33, Issue 12, December 2017, Pages 1582-1595
نویسندگان
Shao-Shi Rui, Yi-Bo Shang, Wenhui Qiu, Li-Sha Niu, Hui-Ji Shi, Shunsaku Matsumoto, Yasuharu Chuman,