Semi-solid metal rheo-cast F357 aluminum plates were joined by autogenous Nd:YAG laser welding and were welded in either the as-cast (F) condition, T4 temper or T6 temper condition. The weldability of this age-hardenable Al–7%Si–0.6%Mg casting alloy was characterized by assessment of the microstructure in the fusion and heat-affected zones and by measurement of the weld-plate tensile and hardness properties. The low heat input provided by the laser welding process resulted in high cooling rates (450–600 K/s) within the fusion and adjacent heat affected zones. This thermal cycle closely resembles quenching practice for standard solution treatments (500–700 K/s) and as a result the T4 condition was maintained during the welding process. Tensile properties equivalent to the parent metal T6 condition were obtained after exposing welded T4 plates to conventional artificial ageing treatment.
► Weldability of rheo-cast F357 in different heat treated conditions, were evaluated.
► The LBW thermal cycle closely resembled the solution treatment quenching practice.
► The thermal cycle resemblance was enough for retention of solid solution in the weld.
► The T4 temper condition was maintained during the welding process.
► Welded T4 plates exposed to artificial ageing, equalled T6 parent metal properties.
Journal: Journal of Materials Processing Technology - Volume 212, Issue 2, February 2012, Pages 465–470