Influence of Sc content on the microstructure and mechanical properties of cast Al-2Li-2Cu-0.5Mg-0.2Zr alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In this work, the influence of Sc content on the microstructure and mechanical properties of cast Al-2Li-2Cu-0.5Mg-0.2Zr alloy was investigated. It was found that the grain size of As-cast alloy was significantly reduced in steps with the increase of Sc addition, accompanied by the arising and increasing of cubic primary Al3(Sc, Zr) phases. No evidence for the presence of the ternary W (Al8âxCu4+xSc) phase was obtained. The volume fraction of nanoscale Al3(Sc, Zr) dispersoids was improved with the increase of Sc content, and the presence of Sc was observed to refine the Sâ² (Al2CuMg) morphology during ageing. The addition of Sc lowered the growth rates of δⲠ(Al3Li) particles and δâ²-Precipitate-free zones (δâ²-PFZs) of the base alloy. The tensile property results showed that, with the increasing Sc content and ageing times, the yield strength (YS) and ultimate tensile strength (UTS) were continuously increased, and the highest elongation of 6.0% was obtained in the 0.2Sc-containing alloy aged for 32â¯h at 175â¯Â°C. The results indicated that the optimal Sc addition in cast Al-2Li-2Cu-0.5Mg-0.2Zr alloy was 0.2â¯wt%.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Characterization - Volume 142, August 2018, Pages 223-236
Journal: Materials Characterization - Volume 142, August 2018, Pages 223-236
نویسندگان
Xiaolong Zhang, Liang Zhang, Guohua Wu, Jiangwei Sun, Mian Rong, Cheng-Chii Hsieh, Yuxiang Yu,