Study on grain boundary character and strain distribution of intergranular cracking in the CGHAZ of T23 steel

Intergranular reheat cracking in the coarse-grained heat-affected zone of T23 steel was produced by strain to fracture tests on a Gleeble 3500 thermal-mechanical simulator. Then the grain boundary character, as well as the strain distribution after reheat crack propagation, was studied by electron backscatter diffraction technique. The results showed that incoherent Σ3 boundaries were seldom found on the prior austenite grain boundaries. Therefore, only the type of random high-angle boundaries played a crucial role in the intergranular cracking. Microstructurally cavities and small cracks were preferentially initiated from high-angle grain boundaries. Low-angle grain boundaries and high-angle ones with misorientation angles less than 15° were more resistant to the cracking. More importantly, the fraction of high-angle grain boundaries increased with the plastic strain induced by both temperature gradient and stress in the coarse-grained heat-affected zone, which contributed to the crack initiation and propagation. Furthermore, the strain distributions in the vicinity of cavities and cracks revealed the accommodation processes of plastic deformation during stress relaxation. It also reflected the strength differences between grain interior and grain boundary at different heat-treated temperatures, which had a large influence on the cracking mechanism.