Controlling the microstructure and mechanical properties of a metastable β titanium alloy by selective laser melting
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Customized titanium alloy devices have become the most attractive orthopaedic implants owing to their effects in mitigating the pain and suffering of patients. This work demonstrates the feasible control of the microstructure, i.e., defects, element diffusion, and phase transformation, and the mechanical properties of a biocompatible Ti-37Nb-6Sn alloy obtained by selective laser melting (SLM). Defects such as voids and unmelted Nb particles, as well grains with random orientation or columnar grains with {100} fiber texture in the as-fabricated Ti-37Nb-6Sn alloy can be modulated by varying the solidification rate and aging effects during the deposition process. A high energy density input promotes the diffusion of Sn from the grain boundaries to the β-matrix, resulting in an increase in the lattice constants of the β-matrix, with low elastic modulus of the as-fabricated Ti-37Nb-6Sn alloy. However, reheating effects promotes the formation of nanoscale α-phase precipitates both at the grain boundaries and in the matrix. The combined effects of rapid solidification and aging induced by reheating result in a metastable β-type Ti-37Nb-6Sn alloy with a Young's modulus of 66â¯GPa, ultimate strength of 891â¯MPa, and elongation of 27.5%. This method can aid the design of customized titanium devices with low elastic modulus for orthopaedic implants applications.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 726, 30 May 2018, Pages 240-250
Journal: Materials Science and Engineering: A - Volume 726, 30 May 2018, Pages 240-250
نویسندگان
Wei Chen, Chao Chen, Xuhui Zi, Xiaofan Cheng, Xiaoyong Zhang, Yong Cheng Lin, Kechao Zhou,