The relationships of microstructure-mechanical properties in quenching and partitioning (Q&P) steel accompanied with microalloyed carbide precipitation
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
A low carbon steel microalloyed with Nb-V-Ti were heat treated by means of two-step quenching and partitioning (Q&P) process after partial austenitization. Combined use of SEM equipped with EBSD, XRD and TEM showed that the microstructure was composed of intercritical polygonal ferrite, tempered lath martensite, secondary twin martensite and carbon-enriched retained austenite, as well as microalloyed carbides (mainly VC) precipitated inside ferrite and martensite. When increasing partitioning time from 0â¯s to 3600â¯s, the volume fraction of retained austenite increased up to 6.5% with mean carbon content in austenite keeping a constant level. The retained austenite kept K-S orientation relationship with adjacent tempered lath martensite and neighboring secondary twin martensite in different martensite packet. As partitioning time increased up to 3600â¯s, the initial lath martensite tempered gradually to ferrite without any cementite formation.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 723, 18 April 2018, Pages 247-258
Journal: Materials Science and Engineering: A - Volume 723, 18 April 2018, Pages 247-258
نویسندگان
Fei Peng, Yunbo Xu, Xingli Gu, Yuan Wang, Xunda Liu, Jianping Li,