Changing distribution and geometry of Sâ² in Al-Cu-Mg single crystals during stress aging by controlling the loading orientation
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The precipitation behavior of Sâ² phase in Al-Cu-Mg single crystals during stress-free and stress aging was investigated by transmission electron microscopy (TEM). Different compressive stress magnitudes and loading orientations were applied to determine their effects on the precipitation of Sâ² in Al-Cu-Mg alloy during stress aging. The results indicate that a noticeable preferential orientation of Sâ² is generated in the sample under applied compressive stress of 33Â MPa loading along close to [001]Al, whilst no obviously preferential orientation of Sâ² can be observed in the sample loaded along close to [101]Al under the same applied stress or even larger applied stress. The precipitation distribution of Sâ² phase during stress aging can be changed by the loading orientation of the applied stress. Moreover, compressive stress aging may lead to Sâ² phase shorter in length, and the length of Sâ² phase shows a decreasing tendency with increasing applied stress, which are associated with the positive misfit between Sâ² and Al matrix.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 650, 5 January 2016, Pages 154-160
Journal: Materials Science and Engineering: A - Volume 650, 5 January 2016, Pages 154-160
نویسندگان
Jiqiang Chen, Zhiguo Chen, Xiaobin Guo, Yunlai Deng,