A research on the microstructure evolution of austenite stainless steel by surface mechanical attrition treatment
ترجمه فارسی عنوان
تحقیق در مورد تحول ریزساختار فولاد ضد زنگ آستنیتی با استفاده از درمان خستگی مکانیکی سطحی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
چکیده انگلیسی
Severe plastic deformation (SPD) was performed on AISI304 stainless steel by surface mechanical attrition treatment (SMAT). The microstructure evolution of the specimens along the depth direction were examined by transmission electron microscope (TEM) and electron backscattered diffraction (EBSD) associated with field emission scanning electron microscope (FESEM). The results show that the specimens by SMAT can be divided into three regions. Region I is the untreated one, where a large number of annealing twins exist. Region II is the small plastic-deformed one, where the grains are deformed by dislocation slipping. Region III is the severe plastic-deformed one, where the grains are deformed by mechanical twinning. The hardness of the untreated and the treated specimens were determined, which shows that the hardness of the untreated specimen (including region I) is about 250HV, while the hardness is uniformly increased from region II to region III, and the largest value appears on the surface. The untreated and the 600 N-treated specimens were determined and observed by X-ray diffractometer (XRD) and confocal laser scanning microscope (CLSM), which shows that the SMAT treated specimen exhibits a layer of ultra-fined γ-Fe grains on the treated surface.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 617, 3 November 2014, Pages 127-138
Journal: Materials Science and Engineering: A - Volume 617, 3 November 2014, Pages 127-138
نویسندگان
S. Liu, S.Y. Gao, Y.F. Zhou, X.L. Xing, X.R. Hou, Y.L. Yang, Q.X. Yang,