Microstructure and mechanical properties of Mgî¸Znî¸Y alloy sheet prepared by hot-rolling
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In this study, the microstructure and mechanical properties of Mgî¸Znî¸Y alloy sheets were investigated. Tensile tests at room temperature were performed along the rolling direction of Mg98Zn1Y1-, Mg96Zn2Y2-, and Mg94Zn3Y3- alloy sheets and their annealed states (773 K for 0.6 ks). These alloy sheets exhibited yield strengths of 261, 317, and 380 MPa, and elongations of 12, 10, and 6%, respectively. The yield strength of a Mgî¸Znî¸Y alloy sheet with Zn and Y contents greater than 2 at% was higher than 300 MPa. The microstructure observations suggested that the alloy sheet strength mainly resulted from (i) the formation of basal texture in the long period stacking ordered (LPSO) phase and (ii) the uniform dispersion of a fine Mg3Zn3Y2 phase. In the annealed state, the yield strength tended to decrease, while the elongation tended to increase. Large elongations of 20% or more were achieved in the Mg98Zn1Y1- and Mg96Zn2Y2 -alloy annealed sheets. The cold workability of the Mgî¸Znî¸Y alloy sheets and an AZ31-O sheet were evaluated, using a V-bending test at room temperature. Both Mg98Zn1Y1- and Mg96Zn2Y2- annealed sheets could be bent without cracking with a minimum bending radius per thickness of 3.3, which was less than that of the AZ31-O sheet. Texture randomization occurred in the Mgî¸Znî¸Y alloy annealed sheets owing to re-crystallization of the Mg phase, which was confirmed by electron backscattering diffraction (EBSD) analysis. Large elongations and good cold workability of the Mgî¸Znî¸Y annealed sheets are presumably attributed to an increase in the randomness of the Mg phase owing to re-crystallization. These results suggested that a Mg alloy sheet of high yield strength or good cold workability could be prepared by controlling the alloy composition and its microstructure in the Mgî¸Znî¸Y alloy system.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 560, 10 January 2013, Pages 216-223