Fatigue damage development in pure polycrystalline magnesium under cyclic tension-compression loading

- Pure Mg exhibits cyclic softening at tensile peak stress at 1% strain amplitude.
- Microcrack initiation mode dependence on loading magnitude.
- Majority of fatigue life spent on initiating microcracks at high strain amplitude.
- Early-stage transgranular crack growth depends on strain amplitudes.