Microstructure change and deuterium permeation behavior of ceramic-metal multi-layer coatings after immersion in liquid lithium-lead alloy
ترجمه فارسی عنوان
تغییر میکروارگانیسم و رفتار نفوذپذیری دوتریوم پوشش های چند لایه فلزات سرامیکی پس از غوطه وری در آلیاژ سرب لیتیوم سرب
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
لیتیوم سرب، مانع نفوذ تریتیوم، خوردگی، اکسید اربیوم،
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی انرژی
انرژی هسته ای و مهندسی
چکیده انگلیسی
For the establishment of liquid tritium breeding concepts, static lithium-lead corrosion tests for single-layer erbium oxide coatings and erbium oxide-metal multi-layer coatings were carried out, followed by deuterium permeation measurements. Grain boundary corrosion of erbium oxide coatings was confirmed by the static immersion tests at 550 and 600 °C. An erbium oxide-iron two-layer coating sustained its structure after lithium-lead immersion at 600 °C for up to 3000 h. The results of gas-driven deuterium permeation measurements for multi-layer coatings immersed at 550 and 600 °C indicated that crystallization and grain growth of erbium oxide would sufficiently occur during the immersion at 600 °C, and then the sample showed lower permeabilities in the first measurements at lower temperature. On the other hand, permeation reduction factors of the sample immersed at 550 °C were estimated to be 100â200 in the temperature range of 400â550 °C. A corrosion layer formed on the coating surface might work as an additional diffusion barrier after the permeation test at 600 °C.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Nuclear Materials and Energy - Volume 16, August 2018, Pages 66-70
Journal: Nuclear Materials and Energy - Volume 16, August 2018, Pages 66-70
نویسندگان
Seira Horikoshi, Moeki Matsunaga, Jumpei Mochizuki, Hikari Fujita, Yoshimitsu Hishinuma, Yasuhisa Oya, Takumi Chikada,