Deuterium retention in tungsten under combined high cycle ELM-like heat loads and steady-state plasma exposure

Enhanced blister formation has been observed under combined loading conditions at power densities close to the threshold for damaging. It is shown that blisters are not mainly responsible for the pronounced increase of the D retention.