Characterization of hot deformation behavior of AA2014 forging aluminum alloy using processing map
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The hot deformation behavior of AA2014 forging aluminum alloy was investigated by isothermal compression tests at temperatures of 350-480 °C and strain rates of 0.001-1 sâ1 on a Gleeble-3180 simulator. The corresponding microstructures of the alloys under different deformation conditions were studied using optical microscopy (OM), electron back scattered diffraction (EBSD) and transmission electron microscopy (TEM). The processing maps were constructed with strains of 0.1, 0.3, 0.5 and 0.7. The results showed that the instability domain was more inclined to occur at strain rates higher than 0.1 sâ1 and manifested in the form of local non-uniform deformation. At the strain of 0.7, the processing map showed two stability domains: domain I (350-430°C, 0.005-0.1 sâ1) and domain II (450-480 °C, 0.001-0.05 sâ1). The predominant softening mechanisms in both of the two domains were dynamic recovery. Uniform microstructures were obtained in domain I, and an extended recovery occurred in domain II, which would lead to the potential sub-grain boundaries progressively transforming into new high-angle grain boundaries. The optimum hot working parameters for the AA2014 forging aluminum alloy were determined to be 370-420 °C and 0.008-0.08 sâ1.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Transactions of Nonferrous Metals Society of China - Volume 27, Issue 8, August 2017, Pages 1677-1688
Journal: Transactions of Nonferrous Metals Society of China - Volume 27, Issue 8, August 2017, Pages 1677-1688
نویسندگان
Peng-wei LI, Hui-zhong LI, Lan HUANG, Xiao-peng LIANG, Ze-xiao ZHU,