Repair behavior of He+-irradiated W-Y2O3 composites after different temperature-isochronal annealing experiments

W-2%Y2O3 composites were prepared by wet chemical and powder metallurgy. Commercial roll tungsten was selected as a comparative sample in the He+ irradiation experiment. The experiment was conducted under He+ beam energy of 50 eV, irradiation dose of approximately 9.9 × 1024 ions/m2, and temperature of 1503-1553 K. The samples were annealed at 1173, 1373, and 1573 K for 1 h. The irradiation surface was observed in situ. The W-2%Y2O3 composites and pure tungsten displayed different grain orientation damage morphologies. In addition, the fuzzy structure was more likely to converge densely at the phase interface. Annealing repairs material surface irradiation damage, whereas the phase interface acts as a He+ migration channel.