Preparation and optical properties of organic/inorganic nanocomposite materials by UV curing process

In this study, photo-polymerized poly(acrylic)/silica hybrid thin films were prepared from various acrylic monomers and monodispersed colloidal silica with the coupling agent, 3-(trimethoxysilyl)propyl methacrylate (MSMA). The silica content in the hybrid thin films varied from 0 to 50 wt.%. The experimental results show that the particle size of silica in hybrid films could be effectively controlled at 15–20 nm as the weight ratio of MSMA to colloidal silica is higher than 0.68 and 0.60 for the poly(methyl methacrylate)/silica (US) and poly(ethylene glycol dimethacrylate-trimethylolpropane trimethacrylate)/silica (UDT) hybrid materials, respectively. The polymerization conversion for US and UDT hybrid materials could reach to 100% and 94.5%, respectively. The comparison of surface roughness with the film thickness is less than 0.10%, indicating the excellent surface planarity of the prepared hybrid thin films. Besides, the prepared hybrid films from the crosslinked acrylic polymer moiety show much better film uniformity, thermal stability and mechanical properties than those obtained from poly(methyl methacrylate). The refractive index decreases with increasing the silica content in the hybrid films. Excellent optical transparency is obtained in the prepared hybrid films. These results show that the prepared hybrid thin films have potential applications as passive films for optical devices.