Electrical and nonlinear optical studies of flux grown Mo and Fe doped KTP crystals

The molybdenum (Mo) and ferric (Fe) doped potassium titanyl phosphate (KTP) crystals were grown by high temperature solution growth (HTSG) technique. The concentration of Mo and Fe in grown crystals was measured by EDX analysis. The SHG efficiencies of the Mo and Fe doped KTP crystals were measured and it was found to be 1.77 and 1.38 times respectively higher than that of pure KTP crystal. The frequency dependence of dielectric constant, loss and ac conductivity was studied at room temperature. The phase matching measurements were made using a Q-switched Nd:YAG laser operating at 1064 nm and the measured phase matching angles are 44.2° and 87.88° for Mo and Fe doped KTP crystals respectively.