Magnetic iron nitrides inspired by historic research on αâ³-Fe16N2
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Strong ferromagnetic materials at room temperature are of interest for various magnetic applications such as magnetic recording, sensors, and motors. Gigantic magnetism expected for αâ³-Fe16N2 thin films had been attracted much attention in terms of its large magnetization per weight in comparison to rare earth iron nitrides R2Fe17N3 because these films are made of only iron and nitrogen. It developed much straggling on iron nitride thin film research but inconsistent results were obtained using different preparation methods. A powdered αâ³-Fe16N2-like compound was prepared by the ammonolysis of fine α-Fe powder in low temperature below 200 °C to clarify the confusion; the magnetism was not large in αâ³-Fe16N2 itself but was increased in the intermediate ammonolysis dual-phase mixture product of the αâ³-Fe16N2-like compound and residual α-Fe. A way to control the magnetic coercivity was subsequently investigated to utilize the larger magnetization in the αâ³-Fe16N2-like compound mixture as magnetic materials similarly to Sm2Fe17N3 bonded magnet. Iron nitrides, zinc blende type γâ³-FeN and rock-salt type γâ´-FeN, also decompose at around 500 °C. Thermal decomposition was a disadvantage in the preparation of the iron nitrides; however, iron nanoparticles dispersed composites in AlN matrix were derived from the iron nitrides (Fe,Al)N by thermal treatment including laser heating. Iron nitrides are thus promising magnetic materials for their potential applications in science and technology.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Progress in Solid State Chemistry - Volume 51, September 2018, Pages 19-26
Journal: Progress in Solid State Chemistry - Volume 51, September 2018, Pages 19-26
نویسندگان
Shinichi Kikkawa, Yuji Masubuchi,