Self-assembled monolayers and chemical derivatization of Ba0.5Sr0.5TiO3 thin films: Applications in phase shifter devices

Thin films of barium strontium titanate (Ba1−xSrx TiO3 (BSTO)) have been used in coupled microstrip phase shifters (CMPS) for possible insertion in satellite and wireless communication platforms primarily because of their high dielectric constant, low loss, large tunability, and good structural stability. In an attempt to improve the figure of merit K (phase shift °/dB of loss) of phase shifters, modification of the metal/BSTO interface of these devices has been done through surface modification of the BSTO layer using a self-assembled monolayer approach. The impact of this nanotechnology promises to reduce RF losses by improving the quality of the metal/BSTO interface. In this study, compounds such as 3-mercaptopropyltrimethoxysilane (MPS), 16-mercaptohexadecanois acid (MHDA) and 3-mercaptopropionic acid (MPA) were used to form the self-assembled monolayers on the BSTO surface. As a result of the previous modification, chemical derivatization of the self-assembled monolayers was done in order to increase the chain length. Chemical derivatization was done using 3-aminopropyltrimethoxysilane (APS) and 16-mercaptohexadecanoic acid. Surface chemical analysis was done to reveal the composition of the derivatization via X-ray photoelectron spectroscopy (XPS) and Fourier Transform Infrared (FT-IR). Low and high frequencies measurements of phase shifters were done in order measure the performance of these devices for insertion in antennas. X-ray photoelectron spectroscopy characterization of modified BSTO thin films with MPS showed a binding energy peak at 162.9 eV, indicative of a possible SO interaction: sulfur of the mercapto compound, MPS, used to modify the surface with the oxygen site of the BSTO thin film. This interaction is at higher binding energies compared with the thiolate interaction. This behavior is observed with the other mercapto compounds such as: MHDA and MPA. An FT-IR analysis present a band at 780 cm−1, which is characteristic of an OSC stretching and reveals the modification of the BSTO thin film by the coupling of the O of the BSTO with the S of the mercapto compound. All the modification using mercapto compounds is through sulfur to the BSTO thin film. MHDA SAM on BSTO thin film was chemically derivatized using APS shown by XPS and FT-IR. The SAMs modified phase shifters showed an improvement in performance with respect to those phase shifters fabricated with standard methods.