A quantitative study of cavity development in the tensile testing of an aluminum metal matrix composite processed by equal-channel angular pressing
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
A metal matrix composite, consisting of an Al-6061 matrix alloy reinforced with 10 vol.% of fine Al2O3 particulates, was processed by equal-channel angular pressing for 1 pass at room temperature and an additional 11 passes at 473 K. Microstructural observations showed the grain size was reduced from â¼3.5 to â¼1.9 μm but the average particulate size remained unchanged at â¼270 nm. Tensile testing was conducted to failure at 873 K on samples cut from the as-received material and from as-pressed billets. Following fracture, quantitative measurements were taken to determine the size and shape of the internal cavities developed during tensile testing. The measurements show cavities form more readily in the as-received condition probably due to the higher flow stresses in this material. The pressed material contained several large cavities oriented parallel to the tensile axis. Calculations show these cavities are consistent with a transition from superplastic diffusion growth to plasticity-controlled growth.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volumes 410â411, 25 November 2005, Pages 402-407
Journal: Materials Science and Engineering: A - Volumes 410â411, 25 November 2005, Pages 402-407
نویسندگان
Megumi Kawasaki, Yi Huang, Cheng Xu, Minoru Furukawa, Zenji Horita, Terence G. Langdon,