Thermal shock cycling behavior of NiCoCrAlYSiB coatings on Ni-base superalloys
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
NiCoCrAlYSiB coatings were obtained using an arc ion plating technique on a directionally solidified Ni-base superalloy. Thermal shock resistance of the bare and coated superalloys were investigated by cycling between high temperature (900, 1000 and 1050 °C) and room temperature (forced water quenching). The microstructure evolution in coatings and the underneath substrates was studied. The results showed that phase transformation from γⲠto γ occurred at the surface of the coated and bare specimens due to the consumption of Al and Ti by oxidation. A directional coarsening of the γⲠprecipitates (γⲠrafting) just beneath the γâ²-impoverishing zone (or interdiffusion zone) is observed. This kind of rafting is believed to come into being from the compressive stresses by temperature gradients due to high cooling rate during cooldown. The relationship between microstructure evolution and cracks formation and propagation is also discussed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 406, Issues 1â2, 15 October 2005, Pages 350-357
Journal: Materials Science and Engineering: A - Volume 406, Issues 1â2, 15 October 2005, Pages 350-357
نویسندگان
Q.M. Wang, H. Li, M.H. Guo, P.L. Ke, J. Gong, C. Sun, L.S. Wen,