Solid state synthesis of nanocrystalline and/or amorphous 50Ni-50Ti alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Solid state synthesis of nanocrystalline and/or amorphous 50Ni-50Ti alloy Solid state synthesis of nanocrystalline and/or amorphous 50Ni-50Ti alloy](/preview/png/9796561.png)
چکیده انگلیسی
A nanocrystalline/amorphous 50Ni-50Ti alloy was produced by solid state synthesis via mechanical alloying from elemental Ti and Ni powders. Using X-ray diffraction analysis and transmission electron microscopy techniques, a mechanically induced solid state reaction of 50Ni-50Ti was investigated. Results showed that nanocrystalline and amorphous Ni-Ti phases were obtained after mechanical alloying. The mechanical alloying of 50Ni-50Ti for 270 ks led to the formation of f.c.c. Ni(Ti) solid solution, characterized by a lattice parameter of 0.3558 nm, crystallite size of 14 nm and lattice strain of 0.98%. The particle size decreased with increasing milling time. The crystallite size of mechanically alloyed 50Ni-50Ti powders was substantially refined as the milling proceeded and the lattice strain increased with the milling time. The steady-state crystallite size was approximately 10-15 nm. The internal lattice strain in Ni-Ti alloy led to the disordering and the subsequent formation of amorphous alloy during mechanical alloying. After heat treatment at 1100 °C, the as-milled powders transformed into B2-NiTi phase and a small amount of Ti2Ni phase.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 392, Issues 1â2, 15 February 2005, Pages 222-228
Journal: Materials Science and Engineering: A - Volume 392, Issues 1â2, 15 February 2005, Pages 222-228
نویسندگان
Y.W. Gu, C.W. Goh, L.S. Goi, C.S. Lim, A.E.W. Jarfors, B.Y. Tay, M.S. Yong,