Fatigue behavior of Zr-Ti-Ni-Cu-Be bulk-metallic glasses
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Fatigue behavior of Zr-Ti-Ni-Cu-Be bulk-metallic glasses Fatigue behavior of Zr-Ti-Ni-Cu-Be bulk-metallic glasses](/preview/png/9802711.png)
چکیده انگلیسی
The high-cycle fatigue (HCF) behavior of the Zr41.2Ti13.8Cu12.5Ni10Be22.5 (in at.%) bulk-metallic glass (BMG) was studied. Two batches of samples that are from different lots (Batches 59 and 94) are employed in present experiments. The HCF experiments were conducted, using an electrohydraulic machine at a frequency of 10Â Hz with a R ratio of 0.1 in air at room temperature and under tension-tension loading, where R=Ïmin./Ïmax.. (Ïmin. and Ïmax. are the applied minimum and maximum stresses, respectively). A high-speed and high-sensitivity thermographic-infrared (IR) imaging system was employed for the nondestructive evaluation of temperature evolutions during fatigue testing. No distinct sparking phenomenon was observed at the final fracture moment for this alloy. The fatigue lifetime of Batch 59 is longer than that of Batch 94 at high stress levels (maximum stresses >864Â MPa). Moreover, the fatigue-endurance limit of Batch 59 (703Â MPa) is somewhat greater than that of Batch 94 (615Â MPa). The vein pattern and liquid droplets were observed in the apparent-melting region along the edge of the fractured surfaces. The fracture morphology suggests that fatigue cracks initiated from casting defects, such as porosities and inclusions, which have an important effect on the fatigue behavior of BMGs.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Intermetallics - Volume 13, Issues 3â4, MarchâApril 2005, Pages 429-435
Journal: Intermetallics - Volume 13, Issues 3â4, MarchâApril 2005, Pages 429-435
نویسندگان
G.Y. Wang, P.K. Liaw, A. Peker, B. Yang, M.L. Benson, W. Yuan, W.H. Peter, L. Huang, M. Freels, R.A. Buchanan, C.T. Liu, C.R. Brooks,