The methodology study of time accelerated irradiation of elastomers
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سطوح، پوششها و فیلمها
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
After irradiation the mechanical properties of samples were measured at room temperature. The changes in 100% modulus suggest that irradiation in 0.5 MPa oxygen increases slightly scission reaction and irradiation at 70 °C increases slightly crosslinking, compared with the results obtained under low dose rate irradiation (the reference condition). The deviation was mostly in ±0.25 for 100% modulus and was ±0.5 for ultimate elongation throughout the all doses, where the value obtained at the reference condition referred to as 1.0. Thus, it was found out that two methods mentioned above are available as time accelerated irradiation conditions.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms - Volume 236, Issues 1â4, July 2005, Pages 229-234
Journal: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms - Volume 236, Issues 1â4, July 2005, Pages 229-234
نویسندگان
Masayuki Ito,