Color center annealing and ageing in electron and ion-irradiated yttria-stabilized zirconia

We have used X-band electron paramagnetic resonance (EPR) measurements at room-temperature (RT) to study the thermal annealing and RT ageing of color centers induced in yttria-stabilized zirconia (YSZ), i.e. ZrO2:Y with 9.5 mol% Y2O3, by swift electron and ion-irradiations. YSZ single crystals with the 〈1 0 0〉 orientation were irradiated with 2.5 MeV electrons, and implanted with 100 MeV 13C ions. Electron and ion beams produce the same two color centers, namely an F+-type center (singly ionized oxygen vacancy) and the so-called T-center (Zr3+ in a trigonal oxygen local environment) which is also produced by X-ray irradiations. Isochronal annealing was performed in air up to 973 K. For both electron and ion irradiations, the defect densities are plotted versus temperature or time at various fluences. The influence of a thermal treatment at 1373 K of the YSZ single crystals under vacuum prior to the irradiations was also investigated. In these reduced samples, color centers are found to be more stable than in as-received samples. Two kinds of recovery processes are observed depending on fluence and heat treatment.