Oxide scale formation and microstructural degradation of conventional, Pt- and Pt/Ir-modified NiAl diffusion coatings during thermocyclic exposure at 1100â°C
Keywords: Intermetallics; EPMA; SEM; Thermal cycling; X-ray diffraction; Oxidation;