Influence of preloading-induced microcracking on the durability of concrete produced with different types of cement
ترجمه فارسی عنوان
تأثیر میکروکراکسیون ناشی از پیش بارگیری بر دوام بتن تولید شده با انواع مختلف سیمان
موضوعات مرتبط
مهندسی و علوم پایه سایر رشته های مهندسی مهندسی عمران و سازه
چکیده انگلیسی
As many concrete structures present premature degradation, large environmental and financial impacts are associated with repairing. It is essential, therefore, to understand mechanical and durability performance of concrete in different conditions of use. This study investigated the chloride penetration resistance of microcracked concretes after being exposed to early loading. So, cylindrical test specimens were prepared with two Brazilian cements, a high initial strength Portland cement and a pozzolanic one, with a water/cement ratio of 0.50. At the age of 3 days, some of the specimens were subjected to a load of 75% of their ultimate compressive strength while reference ones were not preloaded. All specimens were cured by immersion in water tanks for 3, 7, 28 and 91 days. After these periods, preloaded and reference specimens were tested in accordance with chloride penetration resistance (ASTM C1202/12). The best results were observed in the reference samples for both cement types. It was observed a significant reduction in chloride penetration for longer curing times in preloaded and reference specimens due to self-healing. Differences between preloaded and reference specimens were identified, at ages of 3 and 91 days, using scanning electron microscopy and electromagnetic radiation spectra, a non-destructive and low-cost remote sensing technique.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Construction and Building Materials - Volume 189, 20 November 2018, Pages 777-786
نویسندگان
, , ,