Improvement of polypyrrole films for corrosion protection of zinc-coated AZ91D alloy

To improve the protection against the corrosion of AZ91D magnesium alloy provided by conducting polypyrrole (PPy) films, optimization of the electrochemical synthesis of the PPy film was investigated. The bi-layered PPy film was prepared under constant current control, first in a sodium tartrate solution containing molybdate and second in a sodium dodecylsulfate (DS) solution (after the AZ91D alloy was covered by zinc electroplating). Corrosion testing of the zinc-coated AZ91D alloy covered with the PPy film was performed in 3.5% NaCl solution. The more protective PPy film doped with tartrate ions (PPy-Tart film) was formed by the lower current density (CD). Doping of molybdate ions (MoO42−) into the PPy-Tart film significantly improved its corrosion protection properties. When the PPy-Tart-MoO4 layer was covered by an outer PPy layer doped with DS ions, the corrosion protection was further improved. The imposition of ultrasonic waves during the electropolymerization of the inner PPy-Tart-MoO4 layer was effective in the improvement of corrosion protection. The bi-layered PPy-Tart-MoO4/PPy-DS film prepared under ultrasonic irradiation maintained the zinc-coated AZ91D alloy in the passive state during the corrosion test in NaCl solution for 221 h, during which no corrosion products appeared.