Synthesis and characterization of pure poly(acrylate) latexes

For latex characterization and determination of film formation properties, particle size and surface charge densities are determined and thermal analyses were made. The films were characterized by their mechanical properties like hardness, flexibility, adhesion, gloss and UV resistance. Mechanical analysis test results clearly show that among other selected copolymers P(MMA/EA) 1:1.5 copolymer was found to have satisfactory mechanical properties with excellent film forming ability. As AFM studies were in good agreement with mechanical characterization, P(MMA/EA) 1:1.5 copolymer was suggested as a binder that can be used in the paint industry.