On the fabrication of functional graded 3Y-PSZ/316L materials by SPS: Process optimization and characterization of the obtained products

It was found that the temperature interval from 1080 to 1180 °C required for the full consolidation from the 50 vol% composite layer to the 3Y-PSZ one, respectively, can be reached when adopting a specific die configuration where the cross section was varied from 30 to 28 mm, respectively. Correspondingly, the densification level of each layer, as well as the related hardness and fracture toughness properties, were highly enhanced with respect to the standard cylindrical die. In addition, a significant improvement of the material toughness was obtained when the material concentration exponent was decreased from 2 to 1, whereas this effect tends to vanish when such parameter was further reduced to 0.5.