Effect of annealing atmosphere on the structural and electrical properties of BiFeO3 multiferroic ceramics prepared by sol-gel and spark plasma sintering techniques
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Phase-pure BiFeO3 powders were synthesized by sol-gel technique. Based on these powders, high-density BiFeO3 ceramics were prepared by spark plasma sintering (SPS) at 700 °C along with annealing for 2 and 4 h, respectively, at 650 °C under atmospheres of air and oxygen. X-ray diffraction analysis revealed that the 4 h-oxygen-annealed sample contained a single rhombohedral perovskite phase while the samples annealed in the other conditions contained small quantities of impurity phases besides the rhombohedral perovskite phase. The relative density of the 4 h-oxygen-annealed sample was about 96%, being apparently higher than that of the other samples. In comparison with the 4 h-air-annealed sample, the dielectric constant of the 4 h-oxygen-annealed sample was relatively higher. The activation energy for electrical conduction was about 1.17 eV for the 4 h-oxygen-annealed sample while it was about 0.98 eV for the 4 h-air-annealed sample, showing that the former would have a lower room-temperature conductivity (~2.6Ã10â14 S cmâ1) than the latter (~2.1Ã10â13 S cmâ1). It is therefore anticipated that the oxygen-annealed sample could possess better ferroelectric properties as compared to the air-annealed sample.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 42, Issue 6, 1 May 2016, Pages 7328-7335
Journal: Ceramics International - Volume 42, Issue 6, 1 May 2016, Pages 7328-7335
نویسندگان
Ting Wang, S.-H. Song, Meng Wang, J.-Q. Li, M. Ravi,