Effect of agglomeration and calcination temperature on the mechanical properties of yttria stabilized zirconia (YSZ)
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Effect of azeotropic distillation after co-precipitation process of powder synthesis on powders morphology and mechanical properties of yttria stabilized zirconia was studied. The formation of hard or soft agglomerates during drying or calcination of co-precipitated powder can easily be prevented through azeotropic distillation. The powder prepared by direct co-precipitation and azeotropic treatment after co-precipitation process was calcined at different temperatures and was characterized through X-ray diffraction, transmission electron microscope and BET surface area measurement. The calcined powders were compacted uniaxially and sintered in two step sintering process. Sintered, polished and thermally etched samples were observed under scanning electron microscope. Vickers hardness and indentation fracture toughness were estimated. It is observed that reasonably higher density with better hardness and fracture toughness can be achieved for azeotroped samples in same sintering condition. Azeotropic treatment increases the surface area almost three times which helps to achieve better sintering. Pin on disc wear tests against alumina disc at 20Â N and 50Â N loads up to 3000Â m distance were carried out. The wear depth and coefficient of friction for both the material were compared.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 40, Issue 9, Part A, November 2014, Pages 14111-14117
Journal: Ceramics International - Volume 40, Issue 9, Part A, November 2014, Pages 14111-14117
نویسندگان
Ajoy Kumar Pandey, Koushik Biswas,