Preparation of TiC ceramics through aqueous tape casting
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
TiC laminates are prepared through aqueous tape casting and hot pressing technique. Commercial TiC powders were firstly treated and the surface charge was determined through zeta potential measurement. The stability of concentrated TiC suspensions was characterized by rheological test. Results showed that the isoelectric point of as treated TiC particles moved slight toward more acid region, while the zeta potential curves decrease significantly. TiC suspensions exhibit a high degree of particle stabilization. After tape casting, TiC sheets are laminated and hot pressed. The strength and fracture toughness of TiC samples at 1850 °C are 532 MPa and 6.41 MPa m1/2, respectively. The fracture mode is a mixture of intergranular and intragranular type.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 31, Issue 3, 2005, Pages 475-480
Journal: Ceramics International - Volume 31, Issue 3, 2005, Pages 475-480
نویسندگان
Jingxian Zhang, Dongliang Jiang, Qingling Lin, Zhengren Huang,