Fabrication and oxidation behavior of LaB6-ZrB2 composites
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
LaB6-ZrB2 eutectic composites were sintered by hot pressing. The oxidation behavior of LaB6-ZrB2 eutectic composites was studied in the temperature range of 600-1300 °C. It was shown that the sample weight increased with increasing oxidation temperature and prolonging holding time. The rate of weight change was described by kp=6.24Ã10â4exp(â38,940/RT) g2/m2 s, but it changed according to the change of oxidation time at 1200 °C. Weight gain was evident in less than 1 h, but it slowed down subsequently due to the evaporation of B2O3. The rate of weight change increased abruptly at 1300 °C. The oxidation resistance of LaB6-ZrB2 composites was higher than that of monolithic LaB6.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 31, Issue 1, 2005, Pages 15-19
Journal: Ceramics International - Volume 31, Issue 1, 2005, Pages 15-19
نویسندگان
Ruilan Gao, Guanghui Min, Huashun Yu, Shu-qi Zheng, Qingliang Lu, Jiande Han, Weiti Wang,