Electrochemical impedance spectroscopy for the detection of stress corrosion cracks in aqueous corrosion systems at ambient and high temperature

EIS measurements were always performed simultaneously on two identical samples: one stressed with a SSRT or a constant load test and one free of stress. Kramers Kronig Transformations have been used to validate the experimental data obtained with the EIS measurements. It was shown that the phase shift between the two samples could be related to the stress corrosion cracking process. Analysis of the fracture surfaces confirmed that stress corrosion cracks were formed in all three cases.