Microstructural evolution of P92 ferritic/martensitic steel under argon ion irradiation

► Carbide/matrix interfaces in P92 ferritic/martensitic steel were easily damaged. ► Small carbides re-precipitated in matrices after higher dose irradiation. ► Segregation of Cr and W and depletion of Fe in carbides occurred after irradiation.