Effect of RE elements on the microstructural and mechanical properties of as-cast and age hardening processed Mg-4Al-2Sn alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effect of RE elements on the microstructural and mechanical properties of as-cast and age hardening processed Mg-4Al-2Sn alloy Effect of RE elements on the microstructural and mechanical properties of as-cast and age hardening processed Mg-4Al-2Sn alloy](/preview/png/11007769.png)
چکیده انگلیسی
In the present article, the effect of Rare Earth elements on the microstructural development and mechanical properties of as cast and age treated Mg-4Al-2Sn (AT42) alloy is studied. Investigation has been conducted by optical and scanning electron microscope, XRD and tensile tests. Analysis of the data showed that alloy's dendrites turn into larger dendritic structure with sharp and narrow arms from equiaxed rosette type by addition of RE elements. In contrast to the base alloy, aging treatment shows a positive effect on the mechanical properties (yield strength, tensile strength and elongation) of AT42â¯+â¯1RE alloy mainly because of retention of the thermally stable RE containing intermetallics as strong barriers to grain growth. Also, increase of solute aluminum due to the decomposition of Mg17Al12 along with saturated RE elements led to formation of blocky shape Al2RE in the microstructure during aging which enhanced the mechanical properties. It was found that the best result (yield of 70â¯MPa, tensile strength of 168â¯MPa and elongation of 14%) could be achieved by aging the AT42â¯+â¯1RE alloy at 443â¯K (170â¯Â°C) for 8 h. However, mechanical properties of AT42â¯+â¯1RE alloy starts to decrease after exceeding its optimum aging conditions due to the coarsening of intermetallics.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Magnesium and Alloys - Volume 6, Issue 3, September 2018, Pages 309-317
Journal: Journal of Magnesium and Alloys - Volume 6, Issue 3, September 2018, Pages 309-317
نویسندگان
Amir Mahyar Majd, Mohammad Farzinfar, Matin Pashakhanlou, Mohammad Javad Nayyeri,