Quaternized cardo polyetherketone anion exchange membrane for direct methanol alkaline fuel cells

Quaternized cardo polyetherketone (QPEK-C) membranes for alkaline fuel cells were prepared via chloromethylation, quaternization and alkalization of cardo polyetherketone (PEK-C). The chemical reaction for PEK-C modification was confirmed by nuclear magnetic resonance (1H NMR) and energy-dispersive X-ray spectroscopy (EDAX). The QPEK-C membrane was characterized by X-ray photoelectron spectroscopy (XPS) and thermo gravimetric analysis (TG). The ion-exchange content (IEC), water and methanol uptakes, methanol permeability and conductivity of the QPEK-C membranes were measured to evaluate their applicability in alkaline methanol fuel cells. The ionic conductivity of the QPEK-C membrane varied from (1.6 to 5.1) × 10−3 S cm−2 over the temperature range 20–60 °C. The QPEK-C membrane showed excellent methanol resistance. When the concentration of methanol was 4 M, the methanol permeability was less than 10−9 cm2 s−1 at 30 °C.