![عکس صفحه اول مقاله: Structural analysis by synchrotron X-ray diffraction, X-ray absorption fine structure and transmission electron microscopy for aluminum-substituted α-type nickel hydroxide electrode Structural analysis by synchrotron X-ray diffraction, X-ray absorption fine structure and transmission electron microscopy for aluminum-substituted α-type nickel hydroxide electrode](/preview/png/1285207.png)
The detailed structural change in the charge–discharge process was investigated for the 20 mol% aluminum-substituted α-nickel hydroxide by using high-energy synchrotron X-ray diffraction (XRD), X-ray absorption fine structure (XAFS) and transmission electron microscopy (TEM) analysis. The 20 mol% aluminum-substituted α-nickel hydroxide showed the α-Ni(OH)2/γ-NiOOH phase transformation in the charge–discharge process. The structural refinement has been done successfully on the basis of two phase models of the ideal phases and the fault ones, including the occupation sites for the potassium ions and H2O (OH−) molecules. The substituted aluminum ions were situated on both nickel sites and 18h sites in the interlayer. The α-Ni(OH)2 structure would be stabilized by the presence of the aluminum ions on the 18h sites. The α-Ni(OH)2 phases were transformed to the β-Ni(OH)2 phases after 50 cycles because the aluminum ions on the 18h sites would be migrated from the bulk to the surface.
Journal: Journal of Power Sources - Volume 193, Issue 2, 5 September 2009, Pages 871–877