Concentration-gradient LiMn0.8Fe0.2PO4 cathode material for high performance lithium ion battery

• Concentration-gradient LiMn0.8Fe0.2PO4 is constructed through solvothermal method.
• The Mn dissolution of concentration cathode material is suppressed.
• The rate capability of this concentration material is improved.
• The cycle stability is improved, especially at elevated temperature.

It is a great challenge to combine good cycling performance with high rate capability for LiMn1–xMxPO4 cathode materials owing to the Mn dissolution upon cycling and its low electronic/ionic conductivity. Here, we report a novel concentration-gradient structure of LiMn0.8Fe0.2PO4 material constructed by solvothermal treatment. This material shows a linear increase of Mn concentration from the edge to the particle centre, but the inverse trend for Fe concentration, which leads to the formation of Mn-rich phase in bulk and Fe-rich phase at surface. The Fe-rich phase effectively suppresses the corrosion from the electrolyte that minimizes the Mn dissolution and also improves the electronic/ionic conductivity of the surface that decreases the cathode/electrolyte interface resistance. Consequently, this concentration-gradient material achieves superior capacity retention with 98% after 50 cycles at 1 °C even at elevated temperature, and also exhibits an excellent rate capability with the reversible capacity of 130 mA h g−1 at 5 °C rate. These results suggest that the concentration-gradient LiMn0.8Fe0.2PO4 is an ideal type of cathode material for high performance Lithium ion batteries.

Figure optionsDownload as PowerPoint slide