New fluorophosphate Li2−xNaxFe[PO4]F as cathode material for lithium ion battery
موضوعات مرتبط
مهندسی و علوم پایه شیمی الکتروشیمی
پیش نمایش صفحه اول مقاله
New fluorophosphate Li2−xNaxFe[PO4]F as cathode material for lithium ion battery
چکیده انگلیسی


• Li2Fe[PO4]F was prepared from LiNaFe[PO4]F by ion exchange using LiBr in ethanol.
• Li2Fe[PO4]F and LiNaFe[PO4]F crystallize with the Li2Ni[PO4]F-type structure.
• It is different from the Tavorite Li1+xFe[PO4]F- and the layered Na2Fe[PO4]F-type.
• 57Fe Mӧssbauer were collected at different stages of the galvanometric cycling.
• Up to 1 mol of alkali metal is extractable between 1.0 V and 5.1 V vs. Li+/Li.

The new compound Li1.65Na0.35Fe[PO4]F with the Li2Ni[PO4]F structure has been prepared from the analogous LiNaFe[PO4]F phase by ion exchange using LiBr in ethanol at 90 °C. The sample was characterized by powder X-ray diffraction, 57Fe Mӧssbauer spectroscopy, and electrochemical measurements. Li1.65Na0.35Fe[PO4]F crystallizes with orthorhombic symmetry, space group Pnma, with a = 10.5093(5) Å, b = 6.4999(2) Å, c = 11.0483(5) Å, V = 754.70(7) Å3, and Z = 8. The 57Fe Mӧssbauer data collected at different stages of galvanometric cycling confirmed that only 1 mol of alkali metal is extractable between 1.0 V and 5.1 V vs. Li+/Li with a discharge capacity between 135 and 145 mA h g−1. Li/Na electrochemical ion exchange occurs during cycling and leads to a lithium rich phase.