Electronic conductivity of modified La0.95Ni0.6Fe0.4O3−δ perovskites
موضوعات مرتبط
مهندسی و علوم پایه شیمی الکتروشیمی
پیش نمایش صفحه اول مقاله
Electronic conductivity of modified La0.95Ni0.6Fe0.4O3−δ perovskites
چکیده انگلیسی

Phase composition and electronic conductivity of La0.95Ni0.6Fe0.4O3−δ (LNF) modified by small additions (2–10 mol%) of MnO2, TiO2, CeO2 and Sr-containing manganese perovskite were investigated. A-site deficiency was found to be only limited in extent with typically NiO precipitates compensating for the nominal A-site deficiency. The phase composition of modified LNF varies depending on the type and amount of oxide additives. A low level of doping (∼2 mol%) does not change the value of conductivity and temperature of the semiconducting-metallic transition (∼300 °C). However, electronic conductivity of the modified LNF decreases if it contains 5 mol% of oxide additive or more. A decrease in conductivity was observed independently whether a secondary phase is present, solid solutions form or a change in symmetry of the modified LNF occurs. After reduction in argon atmosphere all compositions investigated exhibit semiconducting behaviour in a wide temperature range. Neutron powder diffraction measurements give insight into the mechanism of solid state interaction of LNF with small degrees of oxide additives.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Power Sources - Volume 193, Issue 1, 1 August 2009, Pages 175–179