• We had prepared BICUMGVOX solid electrolyte by sol gel synthetic route.
• The highly conductive γ′–phase was effectively stabilized at room temperature for compositions with x ≥ 0.06.
• The highest value of conductivity 1.5×10–3 S.cm–1 at 300oC obtained for the composition x=0.06.
• This value of conductivity is even higher than the highest reported conductivity uptill now for BICUVOX in the literature at the same temperature.
Samples of Cu(0.10 − x)–Mgx doubly substituted bismuth vanadate, BICUMGVOX (Bi2Cu0.10 − xMgxV0.9O5.35) were synthesized by the citrate sol–gel method. The influence of Cu-Mg substitution on phase stability and oxide-ion performance have been investigated using X-ray powder diffraction (XRPD), FT–IR spectroscopy, differential thermal analysis (DTA) and AC impedance spectroscopy. The highly conductive γʹ–phase was effectively stabilized at room temperature for compositions with x ≥ 0.06 whose thermal stability increases with Mg content. The complex plane plots of impedance for polycrystalline samples showed the variation of equivalent circuit models with composition at isothermal conditions. It was found that the highest value of conductivity 1.5 × 10− 3 S.cm− 1 at 300 °C is obtained from the composition x = 0.06 whose conductivity at 600 °C also reaches its maximum value of 4.9 × 10− 2 S.cm− 1.