The transport properties of La0.1Sr0.9Co0.8Fe0.2O3 − δ (LSCF1982) were measured by oxygen permeation measurements (850 ≤ T/°C ≤ 950, and1 ≤ pO2/atm ≤ 10− 4) and the chemical-diffusion coefficient was extracted from DC conductivity relaxation measurements. The maximum oxygen permeation flux was 1.17 cm3/min cm2 at air/He condition for the 1.5 mm-thick LSCF1982 specimen and the maximum oxygen ion conductivity was around 1 S/cm at 950 °C in nitrogen condition, which strongly supports the potential for catalytic application. The maximum total conductivity was around 1 × 103 S/cm at 500 °C in air, and the oxygen exponent m , applied in the equation σtot=PO2m, was assigned a value of 1/6 at the investigated temperature range. The chemical-diffusion coefficient (D̃) and surface exchange coefficient (κ) were also calculated from the DC conductivity relaxation measurement and the values were best fitted by the following two equations:D˜(cm2/s)=1.04×10°exp−0.58±0.01eVKT, k(cm/s)=1.09×101exp−0.77±0.06eVKT.
Journal: Solid State Ionics - Volume 192, Issue 1, 16 June 2011, Pages 269–274