A lithium phosphorous oxynitride (LiPON) film has been made by sputtering an unsintered Li3PO4 powder target in nitrogen gas. The Li content in the film is only ~ 60% of that in a conventional LiPON film obtained from a Li3PO4 target sintered at 700 °C. The ionic conductivity is 1.7 × 10− 6 S/cm at 25 °C, which is also slightly smaller than that of the conventional film (2.1 × 10− 6 S/cm at 25 °C). The lower content of Li in the new film is compensated by adding Li2O in the target in an amount as much as 50 mol% of Li3PO4. Although the composition of the Li compensated film is almost the same as that of the conventional LiPON film, the ionic conductivity was improved to as large as 3.1 × 10− 6 S/cm at 25 °C. X-ray photoelectron spectra (XPS) revealed that three-coordinated N atoms (P–N Research highlights
► Unsintered Li3PO4 powder target for a LiPON film.
► Li content was about 60% smaller than the conventional LiPON films, and the ionic conductivity was slightly poor.
► The Li content was compensated by adding 50 mol% of Li2O in the target.
► The ionic conductivity was improved to as large as 3.1 × 10− 6 S/cm at 25 °C.
► P–N bonds in the film were mainly three-coordinated, whereas those in the conventional LiPON films are usually two-coordinated.
Journal: Solid State Ionics - Volume 191, Issue 1, 2 June 2011, Pages 49–54