Abnormal Li diffusion in β-LiGa by the formation of defect complex

The diffusion coefficients of Li in the NaTl-type Li intermetallic compound of β-LiGa have been measured by using a short-lived radioactive diffusion tracer. As the tracer, the α-emitting radioisotope of 8Li delivered as the energetic and pulsed beam from Tokai Radioactive Ion Accelerator Complex (TRIAC) was implanted into the β-LiGa compounds with the composition in the range of about 43 to 54 at.% Li. By analyzing the time-dependent yields of the α-particles measured according to the repetition cycle of the beam, the tracer diffusion coefficients were extracted over the wide range of Li composition. Abnormal composition-dependence of Li diffusion coefficients in β-LiGa was observed; the stoichiometric β-LiGa showed the highest diffusivity of Li. By referring to the composition-dependent diffusivity of Li in the iso-structural β-LiAl and β-LiIn, we could identify the abnormal diffusion of Li in very Li-poor composition of β-LiGa. The anomaly has been discussed qualitatively in terms of the formation of defect complex and the interaction between the constitutional defects.